Dentin conditioned with a metal salt-based conditioner

OBJECTIVES: Universal adhesives (UAs) can optionally be applied in either an etch-and-rinse (E&R) or self-etch (SE) bonding mode. As the preferred bonding mode differs for enamel versus dentin, a universal conditioner for both enamel and dentin in replacement of the relatively aggressive phosphoric-acid etchant remains desirable. This study aimed to test if a metal salt-based etchant (ZrO(NO3)2) provides as durable bonding to dentin as a classic E&R or SE bonding mode METHODS: Before applying the UA Adhese Universal ('AdU'; Ivoclar Vivadent) to bur-cut dentin of 24 teeth (n = 8), dentin was conditioned with either (1) an experimental metal salt-based conditioner ('ZON'; Ivoclar Vivadent) or (2) 37% phosphoric acid (Total Etch gel, Ivoclar Vivadent), representing a classic 'E&R' mode; (3) a third experimental group involved AdU applied in SE mode. Bonding effectiveness was determined in terms of immediate ('1w') and aged ('50k' TC) micro-tensile bond strength (μTBS) to bur-cut dentin. Adhesive-conditioned dentin interfacial interactions were characterized by S/TEM. RESULTS: Linear mixed-effects modeling revealed significantly higher immediate μTBS to dentin of ZON_AdU than E&R_AdU, while ZON_AdU performed not significantly different from SE_AdU. No significant differences were found between the three experimental groups after 50k TC (aged μTBS). S/TEM disclosed less exposure of dentinal collagen fibrils when AdU was bonded upon ZON etching than when applied in E&R mode. Moreover, ZON resulted in more hydroxyapatite (HAp) crystals remaining at the bottom of the hybrid layer, while dentinal tubule orifices remained nearly fully closed, by which hardly any resin tags were formed. SIGNIFICANCE: The alternative metal salt-based conditioner revealed at dentin a more HAp-protected hybrid layer with less exposure of collagen fibrils, while a comparable bond strength was obtained to that with a phosphoric-acid E&R as well as with an SE (no conditioner) bonding mode. These findings confirm that the metal salt-based conditioner can be considered as a suitable alternative (enamel/)dentin conditioner to classic phosphoric acid employed in an E&R bonding mode.

Publication year:2022

Accessibility:Open