High critical current density and enhanced pinning in superconducting films of YBa2Cu3O7-δ nanocomposites with embedded BaZrO3, BaHfO3, BaTiO3, and SrZrO3 nanocrystals

Ondertitel:High critical current density and enhanced pinning in superconducting films of YBa2Cu3O7-delta nanocomposites with embedded BaZrO3, BaHfO3, BaTiO3, and SrZrO3 nanocrystals

Chemical solution deposition (CSD) of YBa2Cu3O7−δ (YBCO) nanocomposites from colloidal precursor solutions containing double metal oxide preformed nanocrystals is a promising, cost effective and reproducible approach to produce superconducting films with high critical current density (Jc) and enhanced pinning. Here, the influence of the preformed nanocrystal composition on the microstructure and superconducting properties of the YBCO nanocomposite films is studied, with a focus on establishing a simple and scalable process to grow nanocomposites that can be transferred to grow nano-added coated conductors. Colloidal stable BaZrO3, BaHfO3, BaTiO3 and SrZrO3 nanocrystals (3-6 nm in diameter) were synthesized and added to an environment-friendly low-fluorine YBCO precursor solution. High-quality superconducting layers were grown on LaAlO3 single-crystal substrates from these four nanocomposite precursor solutions in a single deposition process, without the need of a seed layer, yielding Jc of 4-5 MA/cm² at 77 K in self-field. The different YBCO microstructures produced by the four types of nanocrystals and the resulting microstrain of the films are compared and related with the magnetic-field and angular dependence of Jc. We demonstrate the BaHfO3-containing nanocomposite as the best-performing with a homogeneous distribution of nanoparticles with 7 nm in average diameter and a high density of stacking faults, which leads to some of the best superconducting properties ever achieved via low-fluorine CSD. The Jc exhibits a much smoother decay in applied magnetic fields and a much more isotropic behaviour for non-parallel magnetic fields, and the pinning force is increased by a factor of 3.5 at 77 K and 1 T with respect to the pristine film.

Jaar van publicatie:2020

Toegankelijkheid:Open