Sulfobetaine-based ultrathin coatings as effective antifouling layers for implantable neuroprosthetic devices

Foreign body response (FBR), inflammation, and fibrotic encapsulation of neural implants remain major problems affecting the impedance of the electrode-tissue interface and altering the device performance. Adhesion of proteins and cells (e.g., pro-inflammatory macrophages, and fibroblasts) triggers the FBR cascade and can be diminished by applying antifouling coatings onto the implanted devices. In this paper, we report the deposition and characterization of a thin (±6 nm) sulfobetaine-based coating onto microfabricated platinum electrodes and cochlear implant (CI) electrode arrays. We found that this coating has stable cell and protein-repellent properties, for at least 31 days in vitro, not affected by electrical stimulation protocols. Additionally, its effect on the electrochemical properties relevant to stimulation (i.e., impedance, charge injection capacity) was negligible. When applied to clinical CI electrode arrays, the film was successful at inhibiting fibroblast adhesion on both the silicone packaging and the platinum/iridium electrodes. In vitro, in fibroblast cultures, coated CI electrode arrays maintained impedance values up to five times lower compared to non-coated devices. Our studies demonstrate that such thin sulfobetaine containing layers are stable and prevent protein and cell adhesion in vitro and are compatible for use on CI electrode arrays. Future in vivo studies should be conducted to investigate its ability to mitigate biofouling, fibrosis, and the resulting impedance changes upon long-term implantation in vivo.

Publication year:2023

Accessibility:Open